Magnesium aluminate can be obtained by the methods: ceramic method, sol-gel, co-precipitation, hydrothermal and combustion. However, this work presents a simple and low cost route to obtain MgAl2O4 through the gelatin method. The main objective was to use gelatin as an organic precursor and to verify the influence of temperature and time of calcination on the structural and morphological properties of obtained materials. Al and Mg nitrates were used as metal precursors with Al/Mg = 2 ratio. Samples were calcined as follows: 700 ºC, 900 ºC and 1100 ºC during 2 and 4 h. The powders were characterized by TGA, XRD and SEM. A single phase material with a crystallinity of 39.18 - 90.40% and crystallite size in the range of 12.4 to 55.5 nm was obtained. The materials exhibited morphology in the form of plates and small agglomerates. It was found that increasing temperature and time of calcination favored the growth of crystallites and increased crystallinity.

In this work, zinc aluminate spinel was prepared by two methods of directly synthesis (without calcination): microwave assisted combustion and hydrothermal method. The materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and N2-adsorption/desorption isotherms. The XRD patterns confirmed the formation of cubic ZnAl2O4 spinel structure with no secondary phases for both synthesis routes, whereas the hydrothermal method yielded powders with crystallite size 3 times smaller (6.9 nm), as compared to the powders produced by microwave assisted combustion method (25.6 nm). The micrographs revealed agglomerated powders with plate-like morphologies for both routes. Nitrogen adsorption/desorption isotherms (BET) revealed higher surface area (183 m2.g-1) and greater pore volume (0.173 cm3.g-1) for ZnAl2O4 powders prepared by the hydrothermal method.

There is a growing concern on the relationship between anthropogenic carbon dioxide and climate changes. A promising approach is the adsorption technology using mesoporous MCM-41 materials that can be easily synthesized to depict structures adequate to the flow of gas. The aim of this study was to improve the synthesis of MCM-41 using cationic surfactant mixtures and apply the resulting materials to CO2 adsorption. To that end, the simplex-centroid design was applied to optimize CO2 adsorption from seven mesoporous MCM-41 materials synthesized by the hydrothermal method using surfactants from hydrophobic chains of different sizes. The cationic surfactants used were tetradecyltrimetylammonium bromide, cetyltrimethylammonium bromide, trimethyloctadecylammonium bromide and their mixture at ratios of 1:1 and 1:1:1. The CO2 adsorption was investigated using thegravimetric method at 298 K and pressures up to 40 bar. The resulting materials, labelled C17, C19, C21, C17C19, C19C21, C17C21 and C17C19C21, were characterized by XRD, FTIR, TG and SEM and showed significant differences in structure as well as in the mass of CO2 adsorption. The response models showed that the best combination of the surfactants resulted from C17C19 sample, which presented synergistic interactions reaching the highest value of CO2 adsorption (0.62 g CO2/g adsorbent), compared to other samples.

Biodiesel is a fuel renewable, biodegradable and environmentally correct fuel, which can be obtained from the esterification reactions, transesterification and pyrolisis. Montmorillonite is a clay mineral of the smectite group and are of great interest for industrial processes such as catalysis and adsorption. Acid activation of clay minerals is one of the most effective methods proposed to produce active materials. In this work, montmorillonite clay was treated with H2SO4 in different concentrations (0.2 – 0.8 mol L–1), characterized by X-ray diffraction (XRD), infrared spectroscopy (FT-IR) and applied in the catalytic esterification of oleic acid. The results reveal that the clay treated with aqueous solutions 0.8 mol L–1 H2SO4 shows promising catalytic activity toward the studied reaction, with maximum conversion of oleic acid of 65% at 30 °C.